Pro-Series Lab and Performance Tests

Effective: Dec. 9, 2002 - Physical Materials Testing of Cured 1/2 Inch Molded Rubber.

Received: Four (4) cured, 1/2 inch thick, black material sections not identified by Customer.

Content: 95% + recycled tire rubber content, with a virgin rubber binder.

ORIGINAL PHYSICAL PROPERTIES, ASTM D 412-98a, D 2240-02
Die C dumbbells tested at 20 in/min.

		Results:
	Tensile Strength, psi	952
	Ultimate Elongation, %	212
	100% Modulus, psi	355
	200% Modulus, psi	859

COEFFICIENT OF FRICTION, ASTM D 1894-01 (Modified)

Procedure:

Two specimens were prepared from each submitted sample by mounting a 2" x 2" section on a steel plate. Each specimen was pulled at 5 in/min. across a cold-rolled, high carbon steel substrate, polished smooth to the touch. The sample was loaded with a 5 lb weight. The average was reported.

	STATIC,	DYNAMIC,
Textured Side	1.22776	1.09260
Smooth Side	1.20098	1.02618

FLAMMABILITY RESISTANCE, UL-94 HB
5" long x 0.5" wide specimens exposed to flame for 30 seconds. Median results of three specimens reported.

		RESULTS	REQUIREMENTS	PASS/FAIL
	Burn Rate, mm/min.	7.5	40 max	Pass

UV EXPOSURE, ASTM D 925-88(00)
Die C dumbbell specimens exposed 72 hours, ten inches below a 275 W Type RS UV Bulb.

		RESULTS
	Tensile Strength, % change	+5.9
	Elongation, % change	+6.7